|Surface Treatment:||Coated||Alloy Or Not:||Is Alloy|
|Processing Service:||Bending, Cutting||Reflectivity:||About 86%|
|Surface:||Mirror Polished Technology||Mirror Color:||Clear, Bronze, Grey, Blue And Green Etc|
|Tensile Strength:||140N/mm2||Main Grade:||1000 Series, 3000 Series, 5000 Series|
|Main Type:||Mirror, Brushed, Matt, Special Twice||Thickness Tolerance::||+- 0.05mm|
3003 H24 aluminium coil roll,
3003 H24 aluminium coil sheet,
DZSICO SGS BV aluminium coil roll
Aluminium Coil Grade 3003 H24 For Food Container
Aluminum 3003 h24 properties
|Aluminum Alloy 3003 may be a non-heat-treatable 1.2% manganese, 0.12% copper alloy commonly available in flat rolled coil, sheet and plate from a good range of manufacturing mills. it's one among the foremost commonly used of all aluminium alloys, essentially commercially pure aluminium with the addition of manganese to extend its strength about 20%. it's all the superb properties of alloy 1100; excellent corrosion resistance plus the power to be easily drawn or spun, welded or brazed. Alloy 3003 is fairly low strength but it are often hardened to a big degree by cold working,enabling a series of“H” tempers.Alloy 3003 is additionally produced as a bright finish treadplate (also referred to as chequer plate) with industrial and ornamental applications.The alloy is additionally produced as drawn or extruded seamless tube, forgings, wire and bar and foil; these forms are available on indent from Atlas. Alloy 3003 is additionally available as an “Alclad”product with one or each side clad in Alloy7072; again available on indent from Atlas.
Aluminum 3003 h24 Corrosion Resistance
Excellent during a wide selection of atmospheric environments, in food and architectural applications.
Aluminum 3003 h24 Heat Treatment
Alloy 3003 isn't hardenable by heat treatment. It are often significantly hardened by cold work (eg by cold rolling) and various “H”tempers are produced – most ordinarily H12(¼ Hard) and H14 (½ Hard) – also as thesoft annealed Temper O condition.Alloy 3003 is typically supplied in H1x tempers,where the merchandise is strain hardened only;there is not any stabilisation treatment as is common for the 5xxx series alloys.To soften Alloy 3003 it are often annealed byheating to 415°C, hold until uniformtemperature then cool; the speed of cooling isnot important.
Aluminum 3003 h24 Welding
Excellent weldability by all standard methods;gas, electric and resistance welding. GMAW and GTAW are preferred and widely wont to produce structural welds. Filler alloys are usually 1100 although other alloys are possible. Welding of strain hardened tempers will reduce strengths within the heat affected zones.
Aluminum 3003 h24 Machining
Machinability of the softer tempers O and H12 is poor, with the harder tempers like H14
and above being somewhat easier to machine.
Aluminum 3003 h24 Treadplate
Treadplate in alloy 3003 is usually utilized in decorative architectural applications, thanks to its bright reflective finish. it's usually produced during a “1-bar” or “propeller” tread pattern. Alloy 3003 treadplate is out there on indent from Atlas.
Aluminum 3003 h24 Typical Applications
cooking utensils, decorative trim, awnings,siding, storage tanks, chemical equipment.